The evaluation of the removal torque and the histomorphometry of the Ca-P coating surface in rabbit tibia

Affiliations
  • 1Department of Prosthodontics, School of Dentistry, Kyungpook National University, Korea. chlee@knu.ac.kr

Abstract

STATEMENT OF PROBLEM: Surface texture of the implant is one of the important factors of the implant success, especially in the immediate implant loading. Many methods of the surface treatment of implant have developed and introduced. PURPOSE: This study was to evaluate the effects of the Ca-P coating implant crystallized the hydroxyapatite on the surface by the removal torque test and the histomorphometric analysis in vivo. Material and methods: 135 screw type implants, 4.0mm in length and 3.75mm in diameter were used in this study. Implants were divided into 3 groups and treated in the different methods. Group I was not treated, Group II was treated in the SLA method, and Group III was treated in the Ca-P coating with the anodizing method and the hydroxyapatite was crystallized on the surface with the hydrothermal treatment. Firstly, the surface roughness of each group was measured. 45 rabbits were used in this experiment. Two implants were inserted on right tibial metaphysis and one implant was inserted on left side with the alternating order. After the healing periods of 3, 5, and 12 weeks, the rabbits were sacrificed to evaluate the osseointergration by the removal torque test and the histomorphometric analysis. RESULTS: 1. In the analysis for the surface roughness, Group II showed the highest roughness. And Group III showed higher secondly. There was a significant difference one another statistically. 2. In the removal torque test, Group III and II were significantly higher than Group I. There was no statistical difference between Group III and Group II. 3. For all Groups, the removal torque values at 12th week were significantly higher than at 3rd and 5th week. 4. In histomorphometric analysis, the bone implant contact rates of Group III and II were higher than that of Group I at 3rd and 5th week. There was a significant difference at 5th week. 5. In histomorphometric analysis, the bone implant contact rate of Group III and II increased from 3rd week to 5th week, but decreased at 12th week. In Group I, the contact rate at 12th week was significantly higher than at 3rd week and 5th week.

Keyword

Removal torque; Histomorphometry; Ca-P coated implant; SLA method; Anodizing method

MeSH Terms

Durapatite
Rabbits
Tibia*
Torque*
Durapatite
Full Text Links
  • JKAP
Actions
Cited
CITED
export Copy
Close
Share
  • Twitter
  • Facebook
Similar articles
Copyright © 2024 by Korean Association of Medical Journal Editors. All rights reserved.     E-mail: koreamed@kamje.or.kr